The equilibrium orientation relationship between Pt and SrTiO3 and its implication on Pt films deposited by physical vapor phase deposition

Anna Altberg, Galit Atiya, Vissarion Mikhelashvili, Gadi Eisenstein, Wayne D. Kaplan

פרסום מחקרי: פרסום בכתב עתמאמרביקורת עמיתים

תקציר

The equilibrium orientation of Pt in contact with (100)-SrTiO3, at 1050°C and in an Ar/2 % O2 environment, was determined by solid-state dewetting of continuous Pt films on single crystal SrTiO3 substrates. Given the similar lattice parameters between Pt and SrTiO 3, a simple cube-on-cube orientation relationship was expected to form at equilibrium. However, only a preferred orientation of Pt {111} parallel to the SrTiO3 (100) surface formed, without a low-index orientation relationship. It was found that reconstruction of the SrTiO3 surface (a complexion) was responsible for the Pt particle texture. The equilibrium crystal shape of the Pt particles was analyzed and it was found to contain the following facets: {111}, {100}, {110}, and {113}.

שפה מקוריתאנגלית
עמודים (מ-עד)3917-3927
מספר עמודים11
כתב עתJournal of Materials Science
כרך49
מספר גיליון11
מזהי עצם דיגיטלי (DOIs)
סטטוס פרסוםפורסם - יוני 2014

ASJC Scopus subject areas

  • ???subjectarea.asjc.2200.2211???
  • ???subjectarea.asjc.2200.2210???
  • ???subjectarea.asjc.2500.2500???

טביעת אצבע

להלן מוצגים תחומי המחקר של הפרסום 'The equilibrium orientation relationship between Pt and SrTiO3 and its implication on Pt films deposited by physical vapor phase deposition'. יחד הם יוצרים טביעת אצבע ייחודית.

פורמט ציטוט ביבליוגרפי