Characterization of nano-sized particles in 14%Cr oxide dispersion strengthened (ODS) steel using classical and frontier microscopy methods

Yael Templeman, Sergey Rogozhkin, Artem Khomich, Aleksander Nikitin, Malki Pinkas, Louisa Meshi

פרסום מחקרי: פרסום בכתב עתמאמרביקורת עמיתים

תקציר

Oxide dispersion strengthened (ODS) steels exhibit superior mechanical properties and irradiation resistance due to nano-sized oxides, highly dispersed in the metallic matrix. The mechanical properties are affected by the structure, composition, size and density of the nano-sized oxides. Despite numerous reports on the characterization of these oxides, ambiguity regarding their composition, crystallographic structure and orientation relationship with the matrix remains. In the present study, characterization of the crystallographic structure of oxide particles existing in 14%Cr ODS steel was performed using classical and novel transmission electron microscopy (TEM) methods. 3D dispersion, density and composition of these oxides were evaluated by atom probe tomography (APT). Three populations of particles were detected: highly dispersed, 3–20 nm Fe(Cr,Ti,Y)O particles with spinel structure; 50–150 nm YTiO3 and large (100–200 nm) particles identified as cubic TiC. The spinel-type particles displayed Bain and Kurdjumov-Sachs orientation relationships (OR) with the ferritic matrix. Applying electron diffraction tomography, the YTiO3 structure was attributed to the GdFeO3 (distorted perovskite)-type and its lattice parameters were refined as a = 5.46 Å, b = 7.66 Å and c = 5.28 Å. Orientation relationship of the YTiO3 particles and Fe matrix were determined as [110]Fe//[210]oxide and (110)Fe//(002)oxide.

שפה מקוריתאנגלית אמריקאית
מספר המאמר110075
כתב עתMaterials Characterization
כרך160
מזהי עצם דיגיטלי (DOIs)
סטטוס פרסוםפורסם - 1 פבר׳ 2020

ASJC Scopus subject areas

  • ???subjectarea.asjc.3100.3104???
  • ???subjectarea.asjc.2200.2211???
  • ???subjectarea.asjc.2200.2210???
  • ???subjectarea.asjc.2500.2500???

טביעת אצבע

להלן מוצגים תחומי המחקר של הפרסום 'Characterization of nano-sized particles in 14%Cr oxide dispersion strengthened (ODS) steel using classical and frontier microscopy methods'. יחד הם יוצרים טביעת אצבע ייחודית.

פורמט ציטוט ביבליוגרפי