Titanium carbide coating of titanium by cathodic deposition from a carbonate melt

Valery Kaplan, Ellen Wachtel, Igor Lubomirsky

Research output: Contribution to journalArticlepeer-review


The deposition of a TiC coating on a Ti electrode in molten Li 2CO3 at 900°C due to cathodic bias is described. During the first 5-20 min of application of -3V bias with respect to open circuit voltage, the formation of graphite is minimal and the resulting TiC layer is ~10 μm thick. Applying negative bias for longer time results in the formation of graphite dendrites. This behavior can be explained by the fact that the overpotential of CO is lower on TiC than on graphite. The resulting Ti\TiC structure can be employed to good advantage as the anode in the electrolysis of molten Li2CO3 for CO2 to CO conversion for energy storage. It has higher conductivity than the graphite electrode used previously and can be prepared in situ. The process described here can therefore make a valuable contribution to the practical implementation of the electrochemical production of CO. In addition, the fact that the TiC coating is perfectly conformal suggests that the same process can be used as a general method of coating Ti by TiC.

Original languageEnglish
Pages (from-to)E159-E161
JournalJournal of the Electrochemical Society
Issue number11
StatePublished - 2012

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Materials Chemistry
  • Surfaces, Coatings and Films
  • Electrochemistry
  • Renewable Energy, Sustainability and the Environment


Dive into the research topics of 'Titanium carbide coating of titanium by cathodic deposition from a carbonate melt'. Together they form a unique fingerprint.

Cite this