Electronic transport of titanate heterostructures and their potential as channels on (001) Si

Perovskite oxides and their heterostructures have demonstrated considerable potential for devices that require high carrier densities. These oxides are typically grown on ceramic substrates that suffer from low thermal conductivity, which limits performance under high currents, and from the limited size of substrates, which precludes large scale integration and processing. We address both of these hurdles by integrating oxide heterostructures with high carrier density 2D electron gases (2DEGs) directly on (001) Si. 2DEGs grown on Si show significant improvement of the high current performance over those grown on oxide substrates, a consequence of the higher thermal conductivity of the substrate. Hall analysis, transmission line measurements, and the conductance technique are employed for a detailed analysis of the carrier density, contact resistance, mobility, and electron drift velocities. Current densities of 10A/cm are observed at room temperature with 2.9×10¹⁴ electrons/cm² at a drift velocity exceeding 3.5×10⁵cm/s. These results highlight the promise of oxide 2DEGs integration on Si as channels for high electron density devices.