Abstract
The paper deals with the features of obtaining a composite binder containing cement kilns dust, blast furnace slag and Portland cement, in which increased complex activation of blast-furnace granulated slag is achieved, due to the increased content of alkalis in cement dust, as well as the effects of hydroxide and calcium sulphate, contained in the cement. The influence of composition, fineness of grinding and content of chemical additives on the hydration degree and strength of low water demand binders was studied. The optimal relationships between the binder composition and the required fineness of the grinding are established, which ensure the strength characteristics and the hardening speed. The influence of superplasticizers naphthalene formaldehyde and polycarboxylate types, which provide low water demand of binder and high fineness of its grinding, is studied. Using the method of the experiment mathematical planning, equations for the regression of compressive and flexural strengths in different compensations were obtained, which allow predicting strength, taking into account the composition and features of the technology for obtaining the binder.
| Original language | English |
|---|---|
| Pages (from-to) | 361-369 |
| Number of pages | 9 |
| Journal | Revista Romana de Materiale/ Romanian Journal of Materials |
| Volume | 49 |
| Issue number | 3 |
| State | Published - 2019 |
Keywords
- Binder
- Dust
- Grinding
- Hydration degree
- Kiln
- Strength
All Science Journal Classification (ASJC) codes
- General Materials Science