Al Doping for Mitigating the Capacity Fading and Voltage Decay of Layered Li and Mn-Rich Cathodes for Li-Ion Batteries

Li and Mn-rich layered cathodes, despite their high specific capacity, suffer from capacity fading and discharge voltage decay upon cycling. Both specific capacity and discharge voltage of Li and Mn-rich cathodes are stabilized upon cycling by optimized Al doping. Doping Li and Mn-rich cathode materials Li_1.2Ni_0.16Mn_0.56Co_0.08O₂ by Al on the account of manganese (as reflected by their stoichiometry) results in a decrease in their specific capacity but increases pronouncedly their stability upon cycling. Li_1.2Ni_0.16Mn_0.51Al_0.05Co_0.08O₂ exhibits 96% capacity retention as compared to 68% capacity retention for Li_1.2Ni_0.16Mn_0.56Co_0.08O₂ after 100 cycles. This doping also reduces the decrease in the average discharge voltage upon cycling, which is the longstanding fatal drawback of these Li and Mn-rich cathode materials. The electrochemical impedance study indicates that doping by Al has a surface stabilization effect on these cathode materials. The structural analysis of cycled electrodes by Raman spectroscopy suggests that Al doping also has a bulk stabilizing effect on the layered LiMO₂ phase resulting in the better electrochemical performance of Al doped cathode materials as compared to the undoped counterpart. Results from a prolonged systematic work on these cathode materials are presented and the best results that have ever been obtained are reported.