The equilibrium orientation relationship between Pt and SrTiO3 and its implication on Pt films deposited by physical vapor phase deposition

Anna Altberg, Galit Atiya, Vissarion Mikhelashvili, Gadi Eisenstein, Wayne D. Kaplan

نتاج البحث: نشر في مجلةمقالةمراجعة النظراء

ملخص

The equilibrium orientation of Pt in contact with (100)-SrTiO3, at 1050°C and in an Ar/2 % O2 environment, was determined by solid-state dewetting of continuous Pt films on single crystal SrTiO3 substrates. Given the similar lattice parameters between Pt and SrTiO 3, a simple cube-on-cube orientation relationship was expected to form at equilibrium. However, only a preferred orientation of Pt {111} parallel to the SrTiO3 (100) surface formed, without a low-index orientation relationship. It was found that reconstruction of the SrTiO3 surface (a complexion) was responsible for the Pt particle texture. The equilibrium crystal shape of the Pt particles was analyzed and it was found to contain the following facets: {111}, {100}, {110}, and {113}.

اللغة الأصليةالإنجليزيّة
الصفحات (من إلى)3917-3927
عدد الصفحات11
دوريةJournal of Materials Science
مستوى الصوت49
رقم الإصدار11
المعرِّفات الرقمية للأشياء
حالة النشرنُشِر - يونيو 2014

All Science Journal Classification (ASJC) codes

  • !!Mechanics of Materials
  • !!Mechanical Engineering
  • !!General Materials Science

بصمة

أدرس بدقة موضوعات البحث “The equilibrium orientation relationship between Pt and SrTiO3 and its implication on Pt films deposited by physical vapor phase deposition'. فهما يشكلان معًا بصمة فريدة.

قم بذكر هذا