One-dimensional nanoclustering of the Cu(100) surface under CO gas in the mbar pressure range

Baran Eren, Danylo Zherebetskyy, Yibo Hao, Laerte L. Patera, Lin-Wang Wang, Gabor A. Somorjai, Miquel Salmeron

نتاج البحث: نشر في مجلةمقالةمراجعة النظراء

ملخص

The bulk terminated Cu(100) surface becomes unstable in the presence of CO at room temperature when the pressure reaches the mbar range. Scanning tunneling microscopy images show that above 0.25 mbar the surface forms nanoclusters with CO attached to peripheral Cu atoms. At 20 mbar and above 3-atom wide one-dimensional nanoclusters parallel to <001 > directions cover the surface, with CO on every Cu atom, increasing in density up to 115 mbar. Density functional theory explains the findings as a result of the detachment of Cu atoms from step edges caused by the stronger binding of CO relative to that on flat terraces. (C) 2016 Elsevier B.V. All rights reserved.
اللغة الأصليةالإنجليزيّة
الصفحات (من إلى)210-214
عدد الصفحات5
دوريةSurface Science
مستوى الصوت651
المعرِّفات الرقمية للأشياء
حالة النشرنُشِر - سبتمبر 2016
منشور خارجيًانعم

بصمة

أدرس بدقة موضوعات البحث “One-dimensional nanoclustering of the Cu(100) surface under CO gas in the mbar pressure range'. فهما يشكلان معًا بصمة فريدة.

قم بذكر هذا