Influence of Heat Treatment Temperature on Corrosion Characteristics of Biodegradable EW10X04 Mg Alloy Coated with Nd

نتاج البحث: نشر في مجلةمقالةمراجعة النظراء

ملخص

The effect of heat treatment temperature (150, 350, and 550°C) on corrosion of biodegradable EW10X04 Mg alloy coated with Nd was tested in PBS solution. The microstructure was examined by SEM, XRD, and XPS analysis and corrosion resistancewas evaluated by immersion test,potentiodynamic polarization and EIS analysis. Comparatively the complex microstructure of the surface obtained after heat treatment at 350°C has the best corrosion resistance. This was mainly due to the formation of a nearly continuous network of Mg41Nd5 that acts as a protective barrier around α-Mg grains. The heat treatment at 150°C was not effective in creating a similar protective network. In the heat treatment at 550°C, a new intermetallic phase (Mg3Nd)was formed having a detrimental effect on corrosion resistance.

اللغة الأصليةإنجليزيّة أمريكيّة
الصفحات (من إلى)269-276
عدد الصفحات8
دوريةAdvanced Engineering Materials
مستوى الصوت18
رقم الإصدار2
المعرِّفات الرقمية للأشياء
حالة النشرنُشِر - 1 فبراير 2016

All Science Journal Classification (ASJC) codes

  • !!Condensed Matter Physics
  • !!General Materials Science

بصمة

أدرس بدقة موضوعات البحث “Influence of Heat Treatment Temperature on Corrosion Characteristics of Biodegradable EW10X04 Mg Alloy Coated with Nd'. فهما يشكلان معًا بصمة فريدة.

قم بذكر هذا